HUMAN BODY-SAFE EXTERNAL ADDITIVE FOR TONER AND TONER MANUFACTURED USING SAME

Abstract

The present invention provides an external additive for toner, selected from the group consisting of tin oxide fine particles, complex tin oxide fine particles, and a mixture of the same fine particles, wherein the fine particles are (−) charged fine particles having an energy band gap of 3.2 to 3.6 eV, an electronegativity value (χ) of 15 to 18, and a Blow-Off charge amount (uC/g) of −100 to −150. The external additive for toner of the present invention can: replace nano-sized titanium dioxide which has been conventionally used as an external additive for toner; guarantee general consumers using image devices as well as workers in the image industry safety from the harmful influences that may be generated upon exposure to the nano-sized titanium dioxide detached from the surface of a toner in use; and be safe for the human body.

Claims

1. An external additive for toner selected from the group consisting of tin oxide fine particles represented by General Formula of SnaOb (where, “Sn” is tin, “O” is oxygen, and 1.000≤a/b≤2.000 is satisfied), complex tin oxide fine particles represented by General Formula of MxSnyOz (where, M is one or more elements selected from H, an alkali metal, an alkaline earth metal, a rare earth element, Ca, Mg, Sr, Ba, Zr, Ti, Cr, Mn, Fe, Ru, Co, Rh, Ir, Ni, and In, Sn is tin, O is oxygen, 0.001≤x/y≤1 is satisfied, and 1.000≤z/y≤2.000 is satisfied), and a mixture of the fine particles, wherein the fine particles are (−) charged fine particles having an energy band gap of 3.2 to 3.6 eV, an electronegativity value (χ) of 15 to 18, and a Blow-Off charge amount (uC/g) of −100 to −150.

2. The external additive for toner according to claim 1, wherein a diameter of primary particles of the fine particles is 1 nm or more to 200 nm or less.

3. The external additive for toner according to claim 1, wherein a size of a secondary aggregate that is an aggregate of the primary particles is 10 μm or less.

4. The external additive for toner according to claim 1, wherein a specific surface area of the tin oxide and the complex tin oxide fine particles has a value of 5 to 200 m.sup.2/g.

5. The external additive for toner according to claim 1, wherein the fine particles have a composition ratio represented by General Formula of SnaOb (where, “Sn” is tin, “O” is oxygen, and 1.000≤a/b≤2.000 is satisfied).

6. The external additive for toner according to claim 1, wherein the complex tin oxide fine particles represented by General Formula of MxSnyOz has any one or more structures among a tetragonal structure, a cubic structure and a rutile crystalline structure.

7. The external additive for toner according to claim 6, wherein element M is selected from the group consisting of Na, K, Cs, Mg, Ca, Sr, Ba, Fe, Sb, Al, In, Ti, and Zr.

8. An external additive for toner, characterized in that surface of tin oxide fine particles and complex tin oxide fine particles having a size of primary particles of 1 nm to 200 nm is coated with a hydrophobic material showing hydrophobic function.

9. The external additive for toner according to claim 8, wherein the surface of the tin oxide fine particles and the complex tin oxide fine particles are treated and coated with a surface treating agent having the following General Formulae:
(Y)m-Si—(X)n [Si: silicon, (Y+X=4)]
(Y)m-Ti—(X)n, [Ti: titanium, (Y+X=4)]
(Y)m-Zr—(X)n, [Zr: zirconium, (Y+X=4)]
(Y)m-Al—(X)n [Al: aluminum, (Y+Z=3)] where Y: an alkyl group, or a phenyl group, X: an alkoxy group, chloride, bromide, or fluoride.

10. The external additive for toner according to claim 8, wherein the content of the surface treating agent treated at the surface of the tin oxide fine particles and the complex tin oxide fine particles is 0.1 to 50 wt % of the tin oxide fine particles.

11. An external additive for toner, characterized in that surface of toner particles having an average particle diameter of 3 to 8 μm is coated with tin oxide and complex tin oxide fine particles having hydrophobicity within the following range:
Tin oxide/toner particles=0.01 to 1 (weight ratio).

12. The external additive for toner according to claim 2, wherein a size of a secondary aggregate that is an aggregate of the primary particles is 10 μm or less.

13. The external additive for toner according to claim 2, wherein a specific surface area of the tin oxide and the complex tin oxide fine particles has a value of 5 to 200 m.sup.2/g.

14. The external additive for toner according to claim 2, wherein the fine particles have a composition ratio represented by General Formula of SnaOb (where, “Sn” is tin, “O” is oxygen, and 1.000≤a/b≤2.000 is satisfied).

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0027] FIG. 1 shows TEM data of tin oxide nanoparticles.

[0028] FIG. 2 shows FE-SEM data of tin oxide fine particles used as an external additive for toner.

MODE FOR CARRYING OUT THE INVENTION

[0029] Hereinafter, the synthesis of tin(IV) oxide and tin(IV) oxide-based nano-size particles will be explained in more detail. However, the contents of the present invention are not limited only to the explanation in the detailed description.

[0030] Generally, as the raw material of tin oxide, used for the synthesis of tin oxide fine particles and complex tin oxide fine particles, sodium stannate (Na.sub.2SNO.sub.3), potassium stannate (K.sub.2SnO.sub.3), tin(II) chloride, tin(IV) chloride, tin hydroxide (Sn(OH).sub.2), tin hydroxide (Sn(OH).sub.4), tin fluoride (SnF.sub.2), tin(II) dimethoxide, tin(II) diethoxide, tin(II) diethoxide, tin(II) dipropoxide, tin(IV) tetramethoxide, tin(IV) tetraethoxide, tin(IV) tetrapropoxide, or the like may be mainly used, and as the raw material of complex tin oxide, tin compounds such as sodium stannate (Na.sub.2SNO.sub.3), potassium stannate (K.sub.2SnO.sub.3), tin(II) chloride, tin(IV) chloride, tin hydroxide (Sn(OH).sub.2), tin hydroxide (Sn(OH).sub.4), tin fluoride (SnF.sub.2), tin(II) dimethoxide, tin(II) diethoxide, tin(II) diethoxide, tin(II) dipropoxide, tin(IV) tetramethoxide, tin(IV) tetraethoxide, and tin(IV) tetrapropoxide, aluminum compounds represented by sodium aluminate (NaAlO.sub.2), aluminum chloride (AlCl.sub.3), aluminum nitrate (Al(NO.sub.3).sub.3), aluminum acetate, aluminum methoxide, aluminum ethoxide, aluminum propoxide, and aluminum isopropoxide, calcium compounds such as calcium chloride, calcium nitrate, calcium hydroxide, calcium methoxide, and calcium ethoxide, cesium compounds such as cesium chloride, cesium nitrate, cesium hydroxide, cesium fluoride, cesium methoxide, cesium ethoxide, and a cesium metal, magnesium compounds such as magnesium chloride, magnesium nitrate, magnesium hydroxide, magnesium methoxide, and magnesium ethoxide, strontium compounds such as strontium chloride, strontium nitrate, strontium hydroxide, strontium fluoride, strontium methoxide, and strontium ethoxide, barium compounds such as barium chloride, barium nitrate, barium hydroxide, barium fluoride, barium methoxide, and barium ethoxide, indium compounds such as indium chloride, indium nitrate, indium hydroxide, indium fluoride, indium methoxide, indium ethoxide, indium propoxide, and indium isopropoxide, antimony compounds such as antimony chloride, antimony nitrate, antimony hydroxide, antimony fluoride, antimony methoxide, and antimony ethoxide, iron compounds such as iron(II) chloride, iron(III) chloride, iron(II) sulfate, iron(II) nitrate, iron(III) nitrate, iron(II) hydroxide, iron(III) hydroxide, iron(II) fluoride, iron(III) fluoride, iron methoxide, and iron ethoxide, titanium compounds such as titanium(III) chloride, titanium(IV) chloride, titanium oxychloride (TiOCl.sub.2), titanium methoxide, titanium ethoxide, titanium propoxide, and titanium isopropoxide, zirconium compounds such as zirconium(IV) chloride, zirconium oxychloride (ZrOCl.sub.2), zirconium oxynitrate (ZrO(NO.sub.3).sub.2), zirconium methoxide, zirconium ethoxide, zirconium propoxide, zirconium isopropoxide, zirconium butoxide, and zirconium isobutoxide, or the like may be used.

[0031] Tin oxide fine particles and the complex tin oxide fine particles may be prepared using such raw materials through a hydrolysis process and a hydrothermal process, and then, the fine particles may be dried by a freeze drying method, a vacuum drying method, a spray drying method, or the like to minimize the aggregation of such fine particles. And hydrophobic tin oxide fine particles and hydrophobic complex tin oxide fine particles treated with a surface treating agent represented by General Formula of (Y)m-Si—(X)n, (Y)m-Ti—(X)n, (Y)m-Zr—(X)n, or (Y)—Al—(X)n may be prepared to provide the surface of the fine particles thus obtained with hydrophobicity.

[0032] In this case, as an organic compound surface treating agent used as the surface treating agent may include silane coupling compounds such as hexamethyldisilazane, hexadecyltrimethoxysilane, hexadecyltriethoxysilane, hexadecyltrichlorosilane, hexadecylmethyldimethoxysilane, hexadecylmethyldiethoxysilane, hexadecylmethyldichlorosilane, hexadecyldimethylmethoxysilane, hexadecyldimethylethoxysilane, hexadecyldimethylchlorosilane, dodecyltrimethoxysilane, dodecyltriethoxysilane, dodecyltrichlorosilane, dodecyldimethyldimethoxysilane, dodecyldimethyldiethoxysilane, dodecyldimethylchlorosilane, decyltrimethoxysilane, decyltriethoxysilane, decyltrichlorosilane, decylmethyldimethoxysilane, decylmethyldiethoxysilane, decylmethyldichlorosilane, decyldimethylmethoxysilane, decyldimethylethoxysilane, decyldimethylchlorosilane, dimethyldimethoxysilane, dimethyldiethoxysilane, dimethyldichlorosilane, trimethylmethoxysilane, trimethylethoxysilane, and trimethylchlorosilane, titanium coupling compounds such as hexadecyltrimethoxytitanium, hexadecyltriethoxytitanium, hexadecyltrichlorotitanium, hexadecylmethyldimethoxytitanium, hexadecylmethyldiethoxytitanium, hexadecylmethyldichlorotitanium, hexadecyldimethylmethoxytitanium, hexadecyldimethylethoxytitanium, hexadecyldimethylchlorotitanium, dodecyltrimethoxytitanium, dodecyltriethoxytitanium, dodecyltrichlorotitanium, dodecyldimethyldimethoxytitanium, dodecyldimethyldiethoxytitanium, dodecyldimethylchlorotitanium, decyltrimethoxytitanium, decyltriethoxytitanium, decyltrichlorotitanium, decylmethyldimethoxytitanium, decylmethyldiethoxytitanium, decylmethyldichlorotitanium, decyldimethylmethoxytitanium, decyldimethylethoxytitanium, decyldimethylchlorotitanium, dimethyldimethoxytitanium, dimethyldiethoxytitanium, dimethyldichlorotitanium, trimethylmethoxytitanium, trimethylethoxytitanium, and trimethylchlorotitanium, zirconium compounds such as hexadecyltrimethoxyzirconium, hexadecyltriethoxyzirconium, hexadecyltrichlorozirconium, hexadecylmethyldimethoxyzirconium, hexadecylmethyldiethoxyzirconium, hexadecylmethyldichlorozirconium, hexadecyldimethylmethoxyzirconium, hexadecyldimethylethoxyzirconium, hexadecyldimethylchlorozirconium, dodecyltrimethoxyzirconium, dodecyltriethoxyzirconium, dodecyltrichlorozirconium, dodecyldimethyldimethoxyzirconium, dodecyldimethyldiethoxyzirconium, dodecyldimethylchlorozirconium, decyltrimethoxyzirconium, decyltriethoxyzirconium, decyltrichlorozirconium, decylmethyldimethoxyzirconium, decylmethyldiethoxyzirconium, decylmethyldichlorozirconium, decyldimethylmethoxyzirconium, decyldimethylethoxyzirconium, decyldimethylchlorozirconium, dimethyldimethoxyzirconium, dimethyldiethoxyzirconium, dimethyldichlorozirconium, trimethylmethoxyzirconium, trimethylethoxyzirconium, and trimethylchlorozirconium, aluminum compounds such as hexadecyldimethoxyaluminum, hexadecyldiethoxyaluminum, hexadecyldichloroaluminum, hexadecylmethylmethoxyaluminum, hexadecylmethylethoxyaluminum, hexadecylmethylchloroaluminum, hexadecyldimethoxyaluminum, hexadecyldiethoxyaluminum, hexadecyldichloroaluminum, dodecyldimethoxyaluminum, dodecyldiethoxyaluminum, dodecyldichloroaluminum, dodecylmethylmethoxyaluminum, dodecylmethylethoxyaluminum, dodecylmethylchloroaluminum, decyldimethoxyaluminum, decyldiethoxyaluminum, decyldichloroaluminum, decylmethylmethoxyaluminum, decylmethylethoxyaluminum, decylmethylchloroaluminum, decylmethylmethoxyaluminum, decylmethylethoxyaluminum, decylmethylchloroaluminum, dimethylmethoxyaluminum, dimethylethoxyaluminum, and dimethylchloroaluminum, or the like.

Example

[0033] 1. Synthesis of Tin(IV) Oxide Nano-Size Particles and Hydrophobic Coating

[0034] (1) 1 mol/L of sodium stannate (Na.sub.2SnO.sub.3) was weighed, and a sodium stannate (Na.sub.2SnO.sub.3) powder was slowly injected to pure water and dissolved well using a stirrer.

[0035] (2) To the sodium stannate solution obtained in (1), 1 mol/L of nitric acid (HNO.sub.3) prepared in advance was slowly injected to finally adjust the pH of a whole solution to 3 to 3.5.

[0036] (3) Then, tin hydroxide (Sn(OH).sub.4) was obtained, and all unnecessary ion species were removed using pure water and ethyl alcohol.

[0037] (4) Then, the hydrate thus obtained was put in a convection drier and dried at 60° C. for 24 hours.

[0038] (5) Dried tin stannate was heated at 200° C. for 2 hours to synthesize tin(IV) oxide having a specific surface area of 168 m.sup.2/g.

[0039] (6) Hydrophobic coating with dimethyldimethoxysilane, hexamethyldisilazane, or the like was performed with respect to the surface of the tin(IV) oxide nano-size particles obtained in the process of (5) to obtain hydrophobic tin(IV) oxide nano-size particles.

[0040] (7) By Blow-Off test with respect to the product obtained in the process of (6), a value of (−) 130 mV was obtained.

[0041] (8) According to the conventional method of manufacturing toner, the hydrophobic tin(IV) oxide nano-size particles obtained in the process of (7) and the conventionally used additive such as hydrophobic silica were externally treated at the surface of an image material, toner, and the evaluation results on the physical properties on the toner manufactured showed almost the same level as those when using the conventional titanium(IV) dioxide nano-size particles.

[0042] That is, tin(IV) oxide nano-size particles which may replace titanium(IV) dioxide nano-size particles which have harmful controversy to human body, were developed.

[0043] 2. Synthesis of Complex Tin Oxide Fine Particles and Hydrophobic Coating

[0044] (1) 1 mol/L of sodium stannate (Na.sub.2SnO.sub.3) was weighed, 0.01 mol/L of sodium aluminate (NaAlO.sub.2) was weighed, and a sodium stannate (Na.sub.2SnO.sub.3) powder and sodium aluminate were slowly injected to pure water and dissolved well using a stirrer. In this case, the temperature of the pure water was adjusted to about 60° C.

[0045] (2) To a mixture solution of the sodium stannate and sodium aluminate, obtained in (1), 1 mol/L of nitric acid (HNO.sub.3) prepared in advance was slowly injected to finally adjust the pH of a whole solution to 3 to 3.5.

[0046] (3) Then, an aluminum hydroxide (Al(OH).sub.3)-tin hydroxide (Sn(OH).sub.4) complex hydroxide was obtained, and all unnecessary ion species were removed using pure water and ethyl alcohol.

[0047] (4) Then, the complex hydrate thus obtained was put in a convection drier and dried at 60° C. for 24 hours.

[0048] (5) The dried complex hydroxide of aluminum(III) hydroxide-tin(IV) hydroxide was heated at 300° C. for 2 hours to synthesize aluminum(III) oxide-tin(IV) oxide complex oxide fine particles having a specific surface area of 110 m.sup.2/g.

[0049] (6) Hydrophobic coating with dimethyldimethoxysilane, hexamethyldisilazane, decyltrimethoxysilane, or the like was performed with respect to the surface of the aluminum(III) oxide-tin(IV) oxide complex oxide nano-size particles obtained in the process of (5) to obtain hydrophobic aluminum(III) oxide-tin(IV) oxide complex oxide nano-size particles.

[0050] (7) By Blow-Off test with respect to the product obtained in the process of (6), a value of (−) 140 mV was obtained.

[0051] (8) According to the conventional method of manufacturing toner, the hydrophobic aluminum(III) oxide-tin(IV) oxide complex oxide nano-size particles obtained in the process of (7) and the conventionally used additive such as hydrophobic silica were externally treated at the surface of an image material, toner, and the evaluation results on the physical properties on the toner manufactured showed almost the same level as those when using the conventional titanium(IV) dioxide nano-size particles.

[0052] That is, aluminum(III) oxide-tin(IV) oxide complex oxide nano-size particles which may replace titanium(IV) dioxide nano-size particles which have harmful controversy to human body, could be obtained.