ALUMINA SUBSTRATE

Abstract

An alumina substrate on which an AlN layer is formed and that causes less warping, and a substrate material strong enough to withstand normal handling when an AlN crystal is grown upon it, and prevents cracking and fracturing of a grown crystal when stress is applied during growing or cooling. The substrate has a gap and a rare earth element-containing region inside the AlN layer or at the interface between the AlN layer and the alumina substrate. Warping of the AlN layer can be reduced by lattice-mismatch stress being concentrated at the region and releasing of stress by the gap. The region having a concentrating of stress, and the gap having a low mechanical strength, can induce crackings and fracturings. As a result, contamination of crackings and fracturings into the crystal grown on the substrate can be prevented. The region can ensure a level of mechanical strength sufficient for handling.

Claims

1. An alumina substrate comprising: an AlN layer formed on a surface of the alumina substrate, and a rare earth element-containing region and a gap in an interior of the AlN layer or at an interface between the AlN layer and the alumina substrate.

2. The alumina substrate according to claim 1, wherein a content of the rare earth element is 110000 ppm based on Al element ratio.

3. The alumina substrate according to claim 1, wherein a thickness of the AlN layer is 0.02 m to 100 m.

4. The alumina substrate according to claim 1, wherein the alumina substrate is sapphire.

5. The alumina substrate according to claim 4, wherein the AlN layer is mainly composed of a single crystal.

6. The alumina substrate according to claim 2, wherein a thickness of the AlN layer is 0.02 m to 100 m.

7. The alumina substrate according to claim 2, wherein the alumina substrate is sapphire.

8. The alumina substrate according to claim 3, wherein the alumina substrate is sapphire.

9. The alumina substrate according to claim 6, wherein the alumina substrate is sapphire.

10. The alumina substrate according to claim 7, wherein the AlN layer is mainly composed of a single crystal.

11. The alumina substrate according to claim 8, wherein the AlN layer is mainly composed of a single crystal.

12. The alumina substrate according to claim 9, wherein the AlN layer is mainly composed of a single crystal.

Description

BRIEF DESCRIPTION OF THE DRAWINGS

[0024] FIG. 1A is a schematic diagram showing the cross-section of an alumina substrate of the present embodiment, wherein gaps and rare earth elements-containing regions are formed in a dotted state in the way of being sandwiched by the interior of the AlN layer or the interface between the alumina substrate and the AlN layer.

[0025] FIG. 1B is a schematic diagram showing the cross-section of an alumina substrate of the present embodiment, wherein gaps are formed to be touched or sandwiched by the laminar rare earth elements-containing regions.

[0026] FIG. 2 is a diagram showing an example of a flow chart for fabricating an alumina substrate of the present embodiment.

[0027] FIG. 3 is a schematic diagram showing the heating part during the nitriding process of the present embodiment.

[0028] FIG. 4A is a plain view showing a disposition of nitrided substrate and carbon of the present embodiment in Example 1.

[0029] FIG. 4B is a plain view showing a disposition of nitrided substrate and carbon of the present embodiment in Examples 5 and 6.

[0030] FIG. 5A is a schematic diagram showing the first measuring system which will be the reference in the measuring method for the curvature radius of the alumina substrate in the present embodiment.

[0031] FIG. 5B is a schematic diagram showing the optical measuring system after the moving of the irradiation position in the measuring method for the curvature radius of the alumina substrate in the present embodiment.

[0032] FIG. 6A is a schematic diagram showing SEM observation for backscattered electron image of FIB processed cross section of the alumina substrate of the present embodiment in Example 1.

[0033] FIG. 6B is a schematic diagram showing SEM observation for backscattered electron image of the FIB processed cross section of the alumina substrate of the present embodiment in Example 2.

DETAILED DESCRIPTION OF EMBODIMENTS

[0034] The present invention is characterized by the structure in which gaps and rare earth element-containing regions are disposed in an interior of an AlN layer or at an interface between an AlN layer and an alumina substrate. The structure is described using FIG. 1A and FIG. 1B.

[0035] In the present embodiment, rare earth element refers to each element of Y and the lanthanide group. These elements have an ionic radius much bigger than Al, so the effect will be high when they are taken as the elements used in the regions for concentrating stress. Further, rare earth elements have characters that they can form the structure of the present embodiment more easily; further, they are substances which can withstand the AlN crystal growth in a higher temperature for being substances with a high melting point. The rare earth elements are not restricted to be one kind. Several kinds of rare earth elements can be used at the same time.

[0036] FIG. 1A and FIG. 1B are schematic diagrams showing the cross-section of the alumina substrate of the present embodiment. FIG. 1A shows an example in which gaps 31 and rare earth element-containing regions 32 are formed in the interior of AlN layer 30 or at the interface between alumina substrate 33 and AlN layer 30. Each of gaps 31 and rare earth element-containing regions 32 can be disposed separately, and the adjacent gaps 31 and rare earth element-containing regions 32 can be in touch. FIG. 1B shows an example in which rare earth element-containing regions 32 are formed to be laminar, and gaps 31 are disposed to be touched or sandwiched by the laminar rare earth elements-containing layers 32. The laminar rare earth elements-containing layers 32 are disposed in the interior of AlN layer 30 or at the interface between alumina substrate 33 and AlN layer 30. By producing such a structure, stress, which is caused by lattice-mismatch and thermal expansion coefficient difference of alumina substrate 33 and AlN layer 30, can be concentrated in rare earth element-containing region 32. Just by the concentrated stress, stress applied to AlN layer 30 situated in the side closer to the surface than rare earth element-containing region 32 can be reduced, and warping in AlN layer 30 can be decreased. In addition, stress is released due to gaps 31, and thus warping can be decreased. Further, crack generated when excessive stress is applied during the growth of the AlN crystal is induced and propagated to rare earth element-containing region 32 and gap 31, so the AlN crystal can be separated from the alumina substrate without generating crack or fracture in the grown crystals.

[0037] The reason for the concentration of stress in rare earth element-containing region 32 will be described hereinafter. Generally speaking, when two substances with different lattice spacing are combined, stress will be produced because of the lattice-mismatch. Further, when thermal expansion coefficients are different even if their lattice spacings are the same, lattice spacing will change due to temperature fluctuation, so stress caused by lattice-mismatch also will be generated. Compared to the alumina substrate, AlN crystal can obtain larger lattice spacing, and the rare earth element-containing region will obtain much larger lattice spacing. Therefore, when rare earth element-containing region 32 is located between alumina substrate 33 and AlN layer 30 as shown in FIG. 1A and FIG. 1B, stress will be produced nearby the interface formed by alumina substrate 33 and rare earth element-containing region 32. Further, stress will also be produced nearby the interface of rare earth element-containing region 32 and AlN layer 30. That is, two kinds of stress are produced in rare earth element-containing region 32, and thus stress applied on rare earth element-containing region 32 is larger than that produced in AlN layer 30 in the case when only AlN layer 30 is formed on alumina substrate 33. Stress obtained from alumina substrate 33 will be offset just as much as the surplus stress produced in rare earth element-containing region 32, and warping of AlN layer 30 will be decreased.

[0038] When gaps 31 are disposed between alumina substrate 33 and AlN layer 30, crystal lattices of alumina substrate 33 and AlN layer 30 are not bound, so lattice-mismatch will not be generated, and warping can be decreased. On the other hand, the strength of the whole alumina substrate 33 will be decreased as gaps 31 are formed. In the case that such a substrate is used to carry out the growth of the AlN crystal, if lattice-mismatch stress caused by the growth of the crystal is excessive, crack will be generated and propagated due to gaps 31, and thus the grown crystal can be separated from the substrate. However, at the same time if the amount of gaps 31 is too high, crack or fracture will occur even if stress is small in degree of handling, and thus it is difficult to independently operate as a substrate. Additionally, if the amount of gaps is too small, fractures of the grown crystal will occur, and thus it is difficult to stably grow the AlN crystal.

[0039] The inventors of the present invention have found that the same effect as that produced by the gap can be achieved and the strength of substrate can be improved if the gap and the rare earth element-containing region are disposed in combination. Since the outermost surface layer of the alumina substrate of the present invention becomes AlN layer 30, the AlN crystal can be grown on the alumina substrate of the present invention with excellent matching. In addition, if excessive stress caused by lattice-mismatch between the AlN crystal and alumina substrate 33 as well as thermal expansion coefficient difference will be produced along with the growth of the AlN crystal, crack will also be generated and propagated not only by the gaps formed on the alumina substrate of the present invention but also by rare earth element-containing region 32 where stress is concentrated, and thus the grown crystal can be separated from the substrate without bringing damage to the grown crystal. Besides, the crystal lattice of rare earth element-containing region 32 binds with that of alumina substrate 33 and/or AlN crystal 30, so the strength of the whole alumina substrate of the present invention can be prevented from decreasing. Thereby, handling can be conducted in freedom, and various treatments can be subjected to the independent substrate.

[0040] Rare earth element-containing regions 32 and gaps 31 are preferred to be distributed along a surface approximately parallel to alumina substrate surface 33s. It is because that generation and propagation of crack, which is produced when the substrate is subjected to an excessive stress during growing the AlN crystal, is easily induced to a direction approximately parallel to alumina substrate surface 33s, and it is easy to prevent crack from entering the grown crystal. Further, the approximately parallel means that the height difference to the extent that crack propagation to the grown AlN crystal can be suppressed is an allowable level of parallelism.

[0041] The amount of the contained rare earth elements is 1 ppm or more and 10000 ppm or less, and more preferably 1 ppm or more and 1000 ppm or less based on Al element ratio. Thus, warping can be significantly reduced, and crack or fracture can be significantly prevented from occurring in the grown crystal when the AlN crystal is growing on the alumina substrate of the present invention.

[0042] The layer thickness of AlN layer 30 is 0.02 m or more and 100 m or less, and preferably 0.05 m or more and 10 m or less, and more preferably 0.2 m or more and 1 m or less. Thereby, warping can be remarkably reduced. Further, when the AlN crystal is grown on the alumina substrate of the present invention, crack or fracture in the grown crystal can be more significantly prevented from occurring.

[0043] The total length of rare earth element-containing region 32 along a direction approximately parallel to the alumina substrate surface is preferred to be 10% or more and 100% or less relative to the length in the direction approximately parallel to the alumina substrate surface. Thereby, warping can be remarkably reduced. Further, when the AlN crystal is grown on the alumina substrate of the present invention, crack propagation is easily induced in the direction approximately parallel to the alumina substrate surface, and thus crack or fracture in the grown crystal can be more significantly prevented from occurring.

[0044] The total length of gap 31 along a direction approximately parallel to the alumina substrate surface is preferred to be 10% or more and 60% or less relative to the length in the direction approximately parallel to the alumina substrate surface. Thereby, warping can be remarkably reduced. Further, when the AlN crystal is grown on the alumina substrate of the present invention, crack propagation is easily induced in the direction approximately parallel to the alumina substrate surface, and thus crack or fracture in the grown crystal can be more significantly prevented from occurring. Besides, the substrate can be operated without damage in the handling.

[0045] The total length of rare earth element-containing region 32 and gap 31 along a direction approximately parallel to the alumina substrate surface is preferred to be 50% or more and 100% or less relative to the length in the direction approximately parallel to the alumina substrate surface. Thereby, warping can be remarkably reduced. Further, when the AlN crystal is grown on the alumina substrate of the present invention, crack propagation is easily induced in the direction approximately parallel to the alumina substrate surface, and thus crack or fracture in the grown crystal can be more significantly prevented from occurring. Besides, the substrate can be operated without damage in the handling.

[0046] The thickness of rare earth element-containing region 32 and gap 31 in a direction perpendicular to the alumina substrate surface is preferably 50% or less relative to the thickness of AlN layer 30. Thereby, when growing the AlN crystal, crack propagation is easily induced in the direction approximately parallel to the alumina substrate surface, and thus crack or fracture in the grown crystal can be more significantly prevented from occurring.

[0047] When sapphire substrate is used, the formed AlN layer is required to be mainly composed of single crystal. In fact, it is preferred that 50% or more of the total area of the substrate turns to be single crystal, wherein the substrate is the base. Thereby, the cost can be reduced for the fabrication of the devices such as a light emitting device or a power transistor or the like where a semiconductor layer is laminated on a single crystal substrate.

[0048] Hereinafter, an example for fabricating an alumina substrate of the present embodiment is described. Also, an alumina substrate having the same structure as that of the present embodiment can be fabricated by alternative method.

[0049] FIG. 2 illustrates the fabrication flow. As the main process, it is composed of the following a) to d), i.e., a) a process of coating rare earth element-containing raw material on the alumina substrate which will be the base; b) drying process; c) a process of heat treatment for the coated substrate in the air; and d) nitriding treatment process. Further, these processes can be repeated.

[0050] Firstly, the raw material containing the rare earth elements is coated on the alumina substrate. The coating method is not particularly limited. The method can include vacuum method such as sputtering method, electroplating method, spraying method, spin-coating method or the like. In the present example, the raw material is coated by spin-coating method. In spin-coating method, a solution of raw material is required. Thus, the ethanol solution of nitrate of rare earth elements and MOD solution of rare earth elements manufactured by Kojundo Chemical Laboratory Co., Ltd. are used in the present example, and then spin-coated with a speed of 1000 to 3000 rpm for 20 to 120 minutes to form a coating layer. In addition, MOD solution is a solution where organic salts of the rare earth elements are dissolved in a solution with xylene as the main component.

[0051] Next, the heat treatment is subjected in the air. The temperature of the heat treatment depends on the species of rare earth element-containing salt, but it is preferred to be 500 C. to 1400 C., and more preferably to be 600 C. to 1000 C. In such a temperature range, the smoothness of the substrate surface can be maintained, and the coated solution can be heat-decomposed completely and can be oxidized regardless of whether it is an inorganic salt or an organic salt. The treated substrate can be used as nitrided substrate 10.

[0052] Subsequently, the nitriding treatment is performed to form AlN layer 30. FIG. 3 is a schematic diagram showing a heating part of a nitriding furnace. The heating furnace is composed of carbon heater 22, sampling stage 20 and chamber 23 which covers the whole. In chamber 23, gas exhaust port 24 and gas intake port 25 are disposed. Gas exhaust port 24 is connected with a rotary pump (which is not shown in the figure) and a diffusion pump (which is not shown in the figure) and turns out to be a structure which can perform degassing. Further, through gas intake port 25, it turns out to be a structure which can introduce nitrogen gas.

[0053] Alumina plate 13 is disposed on the sampling stage, nitrided substrate 10 and carbon 11 are loaded on it. Further, at the same time, approximately hermetically-closed alumina saggar 12 is disposed on alumina plate 13 to cover the whole of nitriding treatment substrate 10 and carbon 11. Besides, the approximately hermetically-closed state doesn't refer to a sealing property which can block the gas flow entirely, but refers to a sealing property which can suppress the gas flow to some extent. Further, in the case that rare earth element-containing raw material is disposed during the nitriding treatment process, it is disposed to be covered by approximately hermetically-closed alumina saggar 12 just like carbon 11. Further, in the case that rare earth element-containing raw material or carbon is disposed to adhere to the holding jigs, it can be coated inside alumina plate 13 or approximately hermetically-closed alumina saggar 12.

[0054] The heating temperature depends on the rare earth elements, but it is about 1400 to 1800 C. If it is lower than this temperature, the AlN layer cannot be formed sufficiently. On the other hand, if the heating temperature is too high, alumina substrate used as the processed substrate will be deteriorated. Further, carbon 11 is disposed beside the substrate at that time. The amount of carbon 11 would be different according to the processed size and the processed condition, and thus it is not limited and is 0.1 mg or more. If it is too little, the nitriding treatment cannot be performed sufficiently and no or little AlN can be produced. Further, the crystallinity may also be decreased. If it is more than 0.1 mg, the excessive carbon cannot turn to be gas and maintain its original form; thus, it does not have much influence on AlN production. However, sometimes, the flatness of the substrate surface is decreased or different phase is precipitated, so the amount of carbon 11 needs to be adjusted according to the acceptable level.

[0055] Carbon 11 is disposed at the surrounding of nitrided substrate 10. The disposition method of carbon 11 and the form of carbon 11 are not particularly limited. Carbon 11 can be disposed at one place together, and also can be disposed dispersedly. In addition, the carbon can be coated on a holder of alumina saggar 12 or the like. Further, powder, block or rod-like carbon can be disposed.

[0056] According to such a treatment, AlN layer 30 can be formed on the alumina substrate surface. In the case of a sapphire substrate, the formed AlN layer 30 is formed follow the substrate orientation of the foundation. Further, AlN will be generated on the substrate surface even if no Al is contained in the coating raw material. Thus, the AlN is not formed to adhere to the alumina substrate surface but is formed by substituting the oxygen in the alumina substrate nearby the surface with nitrogen. On the other hand, the rare earth elements coated on the substrate surface will mostly disappear through a nitriding treatment. It is thought that they form nitrides or carbides and turn to be gas to disappear.

[0057] An alumina substrate with an AlN layer 30 formed on it without forming rare earth element-containing regions can also be fabricated by turning the entire coated rare earth elements into gas to remove them. The inventors of the present invention considers to left a part of rare earth elements as regions and thus lattice-mismatch stress will be concentrated there. Therefore, they try to remain a part of rare earth elements intentionally. As the result of trials and errors, it is found out that a part of rare earth elements can be remained as rare earth element-containing regions and a part of gasified rare earth elements-containing substance enters inside the alumina substrate of the present embodiment by controlling the thickness and density of the coated layer of the rare earth elements-containing substance, the heat treatment temperature, the nitriding treatment temperature, the duration and the atmosphere control and further adjusting the carbon amount. As a result, the present invention is completed.

[0058] In the present embodiment, the atmosphere is maintained by hermetically-closed heating furnace and approximately hermetically-closed alumina saggar 12, but it is not limited to this. It is considered that as long as the carbon amount and the rare earth elements amount can be controlled, an alumina substrate having the same structure as that of the present embodiment can be obtained even if the heating part is in a gas flow or in an open environment.

[0059] Warping can be evaluated by calculating the curvature radius through a method using surface reflected light. It is described using FIG. 5A and FIG. 5B. Light is irradiated from visible LD or LED light source 41 to arbitrary point 431 on the side formed with AlN layer of nitrided substrate 10 of the present embodiment. The reflected light forms an image on screen 42 and image position 441 is marked. Subsequently, (as shown in FIG. 5A) nitrided substrate 10 is moved only with a distance D in a direction parallel to the screen in a state with the optical system fixed, the irradiation position is changed to position 432. In the same way, the reflected light from irradiation position 432 forms an image on the screen and image position 442 is marked. The distance between the two image positions 441 and 442 is deemed as the displacement X (as shown in FIG. 5B). Further, the distance of nitrided substrate 10 and screen 42 is set as L, and the curvature radius of warping of nitrided substrate 10 is set as R. If L and R are sufficiently larger than D and X, curvature radius R can be approximately calculated by the following formula.

R=2LD/X

[0060] Further, if the displacement vector of irradiation position 432 with irradiation position 431 being the start point and the displacement vector of image position 442 with image position 441 being the start point are parallel, warping of alumina substrate 10 is convex. If they are antiparallel, warping of alumina substrate 10 is concavity.

EXAMPLES

Example 1

[0061] MOD solution was coated on c-plane sapphire substrate with a 4 size of 2 inches by spin coating method under 2000 rpm for 20 seconds, wherein the MOD solution contained Y as the rare element with a concentration of 2 wt %. After coated, the substrate was dried on a hotplate of 150 C. for 10 minutes. Then it was heat treated in air for 2 hours under 600 C. After the heat treatment, the substrate was put on alumina plate 13 with 100 mm square. Further, powder like carbon 11 was disposed in four places around substrate 10 with 20 mg in each place and a total amount of 80 mg. After that, alumina saggar 12 with 75 mm square and a height of 70 mm covered them all. Then, they were set on sampling stage 20. These processes were shown in FIG. 3 and FIG. 4A. The nitriding furnace was an electric furnace of resistance heating type with carbon as the heater. Before heating, degassing was performed using a rotary pump and a diffusion pump to 0.03 Pa, and then nitrogen gas was flowed into the saggar to obtain a pressure of 100 kPa (atmospheric pressure) and after that the flow of nitrogen gas was stopped. The treating temperature of the nitriding treatment was 1750 C., the treating time was set to be 12 hours, and the heating and cooling rate were set as 600 C./h. Further, gas exhaust port 24 were properly opened or closed, and then the pressure in the chamber was adjusted to be 250 kPa at the treating temperature. After cooled to the room temperature, the treated substrate was taken out to evaluate.

[0062] A 10 mm square sample cut out from the vicinity of the center part was used to perform a XRD measurement using Cu as the target. The result confirmed the AlN (002) diffraction ray and thus it could be confirmed as a single crystal or an alignment film along the c axis. On the other hand, crystal phase containing Y could not be found. Further, the intensity ratio of the AlN (002) diffraction ray relative to the sapphire (006) diffraction ray was 65%. Six peaks of six-fold symmetry axis were found in the pole figure measurement using (112) plane and thus it could be confirmed to be a single crystal.

[0063] The curvature radius of the sample was measured using an optical system as shown in FIG. 5A and FIG. 5B. It could be known from the result that the curvature radius was 75 m, and AlN layer forming surface side was convex. Further, the amount of the rare earth element was analyzed using X-ray fluorescence method from AlN layer forming surface side. As a result, 140 ppm of Y atom relative to Al atom number was detected. Subsequently, the cross-section near the center part was FIB processed and then backscattered electron image of SEM was observed. The morphology was schematically shown in FIG. 6A. In the result, a layered white-light-emitting region 52 was observed to be sandwiched by first crystal 50 with a thickness of 0.4 m and second crystal 53. Besides, in the visual field with a length of 10 m, two gaps 31 were observed with being sandwiched by layered white-light-emitting region 52. Both the gaps were roughly rectangular, and the gaps respectively had a shape of length being 1.0 m and thickness being 0.04 m and a shape of length being 0.8 m and the thickness being 0.04 m. Here, the direction parallel to the substrate surface was taken as length, and the vertical direction was taken as the thickness.

[0064] From the result of XRD, it was discovered that first crystal 50 was AlN crystal. Further, it could be confirmed that white-light-emitting region 52 contained elements with larger atomic weight than Al element in view of the property of the backscattered electron image. If the elements used in the treating process were taken into consideration, the element with larger atomic weight than Al element was considered to be Y Further, it was confirmed to be Y by EPMA. In addition, the elements in first crystal 50 and second crystal 53 were also analyzed by EPMA. Thus, first crystal 50 was confirmed to be AlN layer, and second crystal 53 was confirmed to be alumina respectively.

[0065] It could be confirmed from the result of SEM observation that rare earth element-containing regions 32 occupied 82%, gaps 31 occupied 18%, and the total length of rare earth element-containing regions 32 and gaps 31 occupied 100% relative to 10 m of the length direction. In addition, it was known that rare earth element-containing regions 32 and gaps 31 were disposed to be approximately parallel to the substrate surface and the thickness of rare earth element-containing regions 32 and gaps 31 was 10% relative to that of AlN layer 30.

Example 2

[0066] In the 10 mm square samples cut out from Example 1, a sample in the vicinity of the outer circumferential part was performed with XRD measurement, SEM observation and EPMA measurement. In XRD measurement, the result was the same as in Example 1. An AlN (002) diffraction ray was observed and the intensity ratio of AlN (002) diffraction ray relative to sapphire (006) diffraction ray was 55%. Six peaks of six-fold symmetry axis were found in the pole figure measurement using (112) plane and thus the sample could be confirmed to be a single crystal. The curvature radius was 110 m. Further, in the X-ray fluorescence method, 180 ppm of Y atom relative to Al atom number was detected. If compared to Example 1, it was found that if the content of rare earth elements was increased, the curvature radius would be bigger, i.e., warping would be smaller.

[0067] The observed result from the backscattered electron image of SEM was schematically shown in FIG. 6B. White-light-emitting regions 52 and gaps 31 were observed at the interface of first crystal 50 with a thickness of 0.5 m and second crystal 53 as well as in the interior of first crystal 50 nearby the interface. White-light-emitting regions 52 were layered, and three regions were found in an independent form in 10 m length of the visual field. Among the length of the regions, the maximum length was 1 m, and the minimum length was 0.4 m. All the thickness was 0.02 m. On the other hand, five gaps 31 were observed. Among the length of gaps 31, the maximum length was 1 m, and the minimum length was 0.2 m. Besides, the maximum thickness was 0.4 m and the minimum thickness was 0.1 m. It was found that the shapes of gaps were approximately rectangular or approximately triangular. Here, the direction parallel to the substrate surface was taken as length, and the vertical direction was taken as the thickness.

[0068] It was confirmed that white-light-emitting regions 52 were rare earth element-containing regions 32 by the same method as that in Example 1. It could be confirmed from the result of SEM observation that rare earth element-containing regions 32 occupied 28%, gaps 31 occupied 25%, and the total of rare earth element-containing regions 32 and gaps 31 occupied 53% relative to 10 m of the length direction. In addition, it was known that rare earth element-containing regions 32 and gaps 31 were disposed to be approximately parallel to the substrate surface and even the maximum thickness of rare earth element-containing regions 32 and gaps 31 was 8% relative to that of AlN layer 30.

Example 3

[0069] One of 10 mm square samples cut from the vicinity of the center part which was the same in Example 1 was used as the substrate to grow AlN single crystal by a flux method. The flux method was performed by the following conditions. Materials (with a composition as follows, i.e., Si: 35.7 wt %, C: 2.3 wt %, Al: 62.0 wt %, weight: 150 g) were added into a crucible made from yttria-stabilized zirconia and then the crucible was put into the heating region of a high-frequency heating furnace. A stirring jig made from yttria-stabilized zirconia was disposed just above the material, wherein a nitrided sapphire substrate was fixed on the stirring jig. The temperature of the materials in the nitrogen atmosphere was heated to 1600 C. to melt the materials. Then the solution was saturated with nitrogen while stirred by stirring impellers for 5 hours. After that, the nitrided sapphire substrate was contacted to the surface of the solution and rotated at the speed of 100 rpm. At the same time, the temperature of the materials was decreased slowly to grow an AlN single crystal on the sapphire substrate using 20 hours. After the crystal growth was completed, the sapphire substrate was kept away from the solution and the materials were cooled to the room temperature. After being cooled, the sample was taken out from the furnace. It was found that the alumina substrate was peeled in the horizontal direction and the AlN single crystal plate was separated from the part of the sapphire substrate. It was considered that in the growth of the AlN crystal, the rare earth element-containing region withstood the concentrated stress generated by lattice-mismatch and as a result it was peeled spontaneously. The thickness of the AlN single crystal plate was 250 m.

Example 4

[0070] One of 10 mm square samples cut from the vicinity of the center part which was the same in Example 2 was used as the substrate to grow AlN single crystal by the flux method. The conditions of the flux method were the same as those in Example 3. The sample was taken out from the furnace after being cooled. As a result, the alumina substrate was peeled in the horizontal direction and the AlN single crystal plate was separated from the part of the sapphire substrate. It was considered that in the growth of the AlN crystal, the rare earth element-containing region withstood the concentrated stress generated by lattice-mismatch and as a result it was peeled spontaneously. The thickness of the AlN single crystal plate was 250 m.

Example 5

[0071] The c-plane sapphire was cut into 10 mm square to prepare substrate 10 for nitriding treatment. Neodymium (III) nitrate hydrate was dissolved in ethanol to obtain a concentration of 2 wt %. After that, some surfactant was added to fabricate a coating solution. The spin coating was performed under 3000 rpm for 20 seconds. After dried on a hotplate of 250 C. for 10 minutes, the sample was performed with a heat treatment in air for 2 hours under 600 C. After heat treatment, it was disposed on alumina plate 13 with 100 mm square, and further 500 mg of block like carbon 11 was disposed on the two lateral places of substrate 10. The disposition figure was shown in FIG. 4B. A cylindrical alumina crucible with a diameter of 30 mm and a height of 30 mm was used as the approximately hermetically-closed alumina saggar 12. The approximately hermetically-closed state was realized by inverting the alumina crucible and covering substrate 10 and block like carbon 11. The nitriding treatment was performed in the same way as Example 1.

[0072] In XRD measurement, an AlN (002) diffraction ray was discovered, and the intensity ratio of AlN (002) diffraction ray relative to sapphire (006) diffraction ray was 20%. According to SEM observation of backscattered electron image for the FIB processed cross-section, the thickness of first crystal 50 was 0.15 m and white-light-emitting region 52 with a thickness of about 0.02 m was observed. Four gaps with the length of about 0.5 m and the thickness of about 0.02 m were found out in the visual field with the length of 10 m and they were sandwiched by the layered white-light-emitting region 52. Nd atom was contained in the content of 100 ppm based on Al atom number ratio. The curvature radius was 77 m. It was determined according to the results of XRD measurement, SEM observation and EPMA that first crystal 50 was AlN layer, second crystal 53 was alumina, and Nd was contained in the layered white-light-emitting region 52.

Comparative Example 1

[0073] Same treatment was performed in the same way as Example 5 except that a cylindrical alumina crucible with a diameter of 60 mm and a height of 50 mm was used as alumina saggar 12 and the pressure in the chamber was set to be 10 kPa. As a result, the intensity ratio of AlN (002) diffraction ray relative to sapphire (006) diffraction ray was 15%, and the thickness of first crystal 50 was 0.12 m. If compared with Example 5, the intensity of AlN (002) diffraction ray decreased and the thickness of first crystal became thinner. On the other hand, the curvature radius was 15 m, no Nd was detected, and further no gaps were observed. According to the comparison between Example 5 and Comparative Example 1, it could be known that the curvature radius of the alumina substrate in the present embodiment would be larger, i.e., warping would be smaller by containing rare earth elements and gaps.

Example 6

[0074] The c-plane sapphire was cut into 10 mm square to prepare substrate 10 for nitriding treatment. The MOD solution containing Eu as the rare earth element with a concentration of 2 wt % was coated by a spin-coating method with a speed of 2000 rpm for 20 seconds. After coating, the substrate was dried on the hot plate with a temperature of 150 C. for 10 minutes. After that, it was subjected to a heat treatment at 600 C. for 2 hours in the air. The nitriding treatment was performed in the same way as Example 5 except the treating temperature was set to be 1600 C.

[0075] In XRD measurement, an AlN (002) diffraction ray was discovered, and the intensity ratio of AlN (002) diffraction ray relative to sapphire (006) diffraction ray was 32%. According to SEM observation for FIB processed cross-section, the thickness of first crystal 50 was 0.2 m and white-light-emitting region 52 was present in layer. It was confirmed that the thickness of white-light-emitting region 52 was about 0.02 m. Further, two gaps with the length of about 0.8 m to 1.5 m and the thickness of about 0.02 m were found in the visual field with the length of 10 m and they were sandwiched by the layered white-light-emitting region 52. The curvature radius was 35 m. In addition, Eu atom was contained in the content of 50 ppm based on Al atom number ratio. It was determined according to the results of XRD measurement, SEM observation and EPMA that first crystal 50 was AlN layer, second crystal 53 was alumina, and Eu was contained in the layered white-light-emitting region 52.

[0076] The alumina substrate of the present invention not only can be used as a substrate for growing single crystal such as AlN or the like, but also can be used in a substrate for light emitting element and semiconductor element, or a substrate of the product in the field which using the high thermal conductivity of AlN.

[0077] Further, the alumina substrate of the present invention itself can also be used directly as long as the utility value in industry was not damaged. That is, as long as the amount of the contained rare earth elements is in the allowed range, the alumina substrate can also be used as a high thermal conductivity substrate, a substrate for surface acoustic wave or a piezoelectric substrate.

DESCRIPTION OF REFERENCE NUMERALS

[0078] 10 nitrided substrate [0079] 11 carbon [0080] 12 alumina saggar [0081] 13 alumina plate [0082] 20 sampling stage [0083] 22 carbon heater [0084] 23 chamber [0085] 24 gas exhaust port [0086] 25 gas intake port [0087] 30 AlN layer [0088] 31 gap [0089] 32 rare earth element-containing region [0090] 33 alumina substrate [0091] 33s alumina substrate surface [0092] 41 visible LD or LED light source [0093] 42 screen [0094] 431 the irradiation position of the light in an arbitrary point on the side formed with AlN layer of nitrided substrate 10 of the present embodiment [0095] 432 the irradiation position of the light after nitrided substrate 10 of the present embodiment is moved parallel to screen 42 [0096] 441 the imaging position of the reflected light imaged on the screen corresponding to irradiation position 431 of the light [0097] 442 the image position of the reflected light imaged on the screen corresponding to irradiation position 432 of the light [0098] 50 first crystal [0099] 52 white-light-emitting region [0100] 53 second crystal